The wear of artificial finger joints using different lubricants in a new finger wear simulator

Lookup NU author(s): Professor Tom Joyce

Downloads

Full text for this publication is not currently held within this repository. Alternative links are provided below where available.


Abstract

A new design of finger wear simulator has been manufactured. The simulator is a dual cycle machine, interspersing dynamic flexion–extension motion, where the loads were 10–15 N, with periods of a static 100 N ‘pinch’ load. Also, a two-piece finger prosthesis has been designed and manufactured from silane cross-linked polyethylene. Using the simulator, a comparison of the wear of the cross-linked polyethylene prosthesis was undertaken, with Ringer solution, distilled water and dilute bovine serum as the lubricants. Each test was run at 37°C and included a control prosthesis to account for lubricant uptake. All prostheses came from the same batch, having a gel content of 87%. In total, testing exceeded 27 million cycles. With bovine serum, the total wear factor for the prosthesis was 0.07×10−6 mm3/N m. With Ringer solution it was 0.98×10−6 mm3/N m and with distilled water the wear factor was 0.60×10−6 mm3/N m. This order of results matched that found with pin on plate wear tests using these same three lubricants. The lower wear found with bovine serum may have been due to the positive boundary lubricating effects of the proteins within the serum. Lubricant uptake was greater and more significant in the bovine serum test.


Publication metadata

Author(s): Joyce TJ; Unsworth A

Publication type: Article

Publication status: Published

Journal: Wear

Year: 2001

Volume: 250

Issue: 1-12

Pages: 199-205

ISSN (print): 0043-1648

ISSN (electronic): 1873-2577

Publisher: Elsevier

URL: http://dx.doi.org/10.1016/S0043-1648(01)00657-3

DOI: 10.1016/S0043-1648(01)00657-3

Notes: 13th International Conference on Wear of Materials


Altmetrics

Altmetrics provided by Altmetric


Actions

Find at Newcastle University icon    Link to this publication


Share