Modelling and full-scale trials to investigate fluid pressurisation of rolling contact fatigue cracks

Lookup NU author(s): Dr David Fletcher, Dr Paul Hyde, Professor Ajay Kapoor

Downloads

Full text for this publication is not currently held within this repository. Alternative links are provided below where available.


Abstract

Fluid penetration of cracks has been regarded as an important mechanism of crack growth for inclined surface breaking cracks under contact loading since the 1930s. However, there are only limited cases in which it is realistic to assume fluid is sealed in and pressurised by wheels crossing cracks of complex three-dimensional morphology in rolling contact fatigue affected rail. To investigate, modelling to predict crack growth rates was conducted following experimental verification that fluid penetration occurs for a full size rail-wheel contact. A fluid filled crack beneath a three-dimensional elliptic contact was modelled through development of an existing two-dimensional model. Stress intensity factor results from this model were in good agreement with available literature values, indicating very high growth rates for cracks containing pressurised fluid. At larger crack sizes, for which it was assumed the contact could not seal fluid inside the crack, a shear mode crack growth model was applied. This predicted much lower crack growth rates, of around ten times the rail wear rate, indicating a crack growing sufficiently fast to "keep ahead" of wear, but not unrealistically fast. Further work to correlate the predictions of the fluid pressurisation model with field measurements was suggested. © 2008 D.I. Fletcher.


Publication metadata

Author(s): Fletcher DI, Hyde P, Kapoor A

Publication type: Article

Publication status: Published

Journal: Wear

Year: 2008

Volume: 265

Issue: 9-10

Pages: 1317-1324

ISSN (print): 0043-1648

ISSN (electronic): 1873-2577

Publisher: Elsevier BV

URL: http://dx.doi.org/10.1016/j.wear.2008.02.025

DOI: 10.1016/j.wear.2008.02.025


Altmetrics

Altmetrics provided by Altmetric


Actions

    Link to this publication


Share